A Novel Method to Assess Wear Rates of Retrieved Tibial Inserts Following in-vivo Use

Ultra-high molecular weight polyethylene (UHMWPE) on cobalt chrome is the bearing couple of choice for total knee arthroplasty. The number of patients undergoing total knee arthroplasty has been steadily growing and is projected to continue increasing rapidly in the near future. Many of these patients are younger and more active and therefore need a longer lasting device. However, many of these devices fail prematurely and often the primary reason for failure and ultimately revision is due to wear related issues. Therefore, examining how wear rates of the UHMWPE tibial insert change during in-vivo use can help elucidate the mechanisms of accelerated wear and hopefully aid in finding solutions to combat wear related failures.;Different crosslinking treatments have been employed by manufacturers to improve wear resistance of the polyethylene. While this has been shown to be an effective way to reduce wear, crosslinking has led to other issues such as oxidative instability and a decline in mechanical properties. The purpose of this body of work is to examine how changes in oxidation, after in-vivo use, affect wear resistance.;A novel testing method was developed to test the native articular surface from retrieved tibial inserts in a laboratory Pin-on-Disk (POD) simulator. The method was validated using short-duration implant articular surfaces and non-articular control pins. In the absence of high surface oxidation or severe surface damage, the articular surface pins had comparable steady state wear rates to their bulk counterparts.;Tests of devices with longer in-vivo service show chemical changes consistent with a free-radical mediated oxidation mechanism. Tribological assessment of the articular surfaces shows increasing wear rates as a function of oxidation. While this relationship has been hypothesized in the literature, these experiments represent the first physical demonstration of the phenomenon. The wear mechanism is further explored through infrared spectroscopy, assessment of the wear scar, and documentation of evolution of the contact surfaces in the articulation.