| The photocatalytic properties of ceramic ultrafilters have been utilized in the development of a novel in-situ membrane cleaning process for ultrafiltration membranes fabricated from titania. The use of the photoactive membrane layer mitigates the effects of foulants in the system, thereby yielding an increase in the observed overall flux without sacrificing rejection of the solute by the membrane.; Photocatalytic membranes of titania supported on porous tubes of alpha-alumina were fabricated using sol-gel techniques. These membranes were developed on the basis of the results of two-level factorial experimental designs. Electron microscopy and x-ray spectrometry were employed to evaluate coverage of the support by the membrane, the thickness of the membrane, and the presence of defects in the membrane.; The photocatalytic membrane system was characterized to determine both morphological and performance parameters. Morphological parameters included the pore diameters, Darcy coefficients, and the individual resistances associated with each of the porous layers comprising the composite photocatalytic membrane. Performance parameters included the nominal molecular weight cutoff values of the ceramic membranes, the rate of permeation of pure solvent in the presence and the absence of UV illumination; through the porous layers of interest, and the ability of the photocatalytic membrane to resist fouling and maintain permselectivity in the presence of UV illumination.; The photocatalytic membranes were used to ultrafilter aqueous solutions of polymeric organic foulants present at an initial concentration of 1 x 10-3 M. Formation of a gel layer of foulant on the surface of the membrane was observed in the presence and in the absence of UV radiation; however, the results of permeability experiments indicated that formation of this foulant layer was significantly retarded (by a factor of two) in the presence of UV radiation. Improvement in the flow rate of permeate through the membrane was attributed to photocatalytic degradation of solute molecules comprising the indicated gel layer. This hypothesis was confirmed by mass spectrometry measurements. In both the presence and the absence of illumination, rejection of solutes by the membrane was greater than 97%, as determined by total organic carbon analyses of the permeate. |