Development of textured magnesium oxide templates and bicrystals using ion beam assisted deposition

Recently, there has been an increased research effort in the deposition of near-single-crystal thin films on substrates that do not provide a template for epitaxial crystalline film growth. Ion beam assisted deposition (IBAD) has been demonstrated as one of the most promising methods to artificially control the texture in thin films.; Biaxially textured MgO templates of 10 nm thickness were successfully fabricated on glass and silicon substrates without any buffer layers using IBAD. This work has shed insights on several issues. First, surface morphology ∼ 1 nm or better is only a necessary condition for textured IBAD-MgO, but not a sufficient condition. Additional surface preparation must be provided for nucleation and subsequent formation of the textured IBAD-MgO templates. Second, the role of buffer layer on IBAD-MgO texturing. It was found that the ion beam pre-exposure of the substrates prior to IBAD processing provided a sufficient condition for the nucleation and subsequent texture formation of the IBAD grown films. The ion pre-exposure replaced the need for buffer layers in silicon and glass substrates. Finally, by pre-exposing the substrates to Ar + ions, it was found that the ion beam modified the surface and improved the surface roughness of the glass substrates.; Textured MgO epi templates were demonstrated for the first time on polymer based substrates (polyimide). This is a crucial step in the realization of epitaxial suspended devices. To achieve an epitaxial film on a sacrificial layer, an epitaxial template film must first be grown prior to subsequent film growth. The role of ion pre-exposure and buffer layer on texture formation was investigated in this part of the work.; This thesis also presents groundbreaking results on the fabrication of bicrystal MgO films and bicrystal networks using ion beam assisted deposition. Highly oriented bicrystals, with a common (100) out-of-plane orientation and (110) in-plane orientations having a tilt angle of 45° and 20° have been successfully fabricated. This method has also been used to fabricate two dimensional bicrystal MgO networks in the micrometer scale. The same strategy can be applied to generate nanometer scale bicrystal networks of desired patterns.