Pyroelectric response of perovskite heterostructures incorporating conductive oxide electrodes

The use of imaging technologies has become pervasive in many applications as the demand for situational awareness information has increased over the last decade. No better example of the integration of these technologies can be found than that of infrared or thermal imaging. This dissertation, in the field of thermal imaging, has been motivated by the desire to advance the technology of uncooled, thin-film pyroelectric sensors and focuses on the materials and structures from which the detector elements will be built.; This work provides a detailed study of the pyroelectric response of the La-Sr-Co-O/Pb-La-Zr-Ti-O/La-Sr-Co-O (LPL) structure. The LPL structure was chosen based on the needs of thin film detectors, the unique properties of the conductive oxide La-Sr-Co-O (LSCO), and the broad applicability of the Pb-La-Zr-Ti-O (PLZT) material system. Epitaxial heterostructures were grown by pulsed laser deposition on single-crystal oxide substrates. Using the oxygen pressure during cooling and heating of the LSCO layer as a key variable, we have been able to produce structures that have a pronounced internal field in the as-grown state. In these capacitors, where the bottom electrode has a large concentration of oxygen vacancies, we have discovered very large pyroelectric responses that are 10 to 30 times larger than expected of PLZT-based pyroelectric materials (typical values are 20 to 40 nCcm-2K -1). The enhanced pyroelectric responses are very repeatable, stable over time, and distinctly different from responses attributed to thermally stimulated currents. Detailed positron annihilation spectroscopy measurements reveal that there is indeed an oxygen concentration gradient across the capacitor. Based on the results of this study, I will present an analysis of the enhanced pyroelectric response. Although the enhanced response has been correlated with high concentrations of oxygen vacancies in the PLZT film and LSCO electrodes, the mechanism by which the large pyroelectric currents are generated is not yet known. It is likely, however, that a sub-lattice of oxygen and lead vacancies forms the enhanced dipoles and that due to the highly defective nature of the lattice, has a large effective pyroelectric coefficient.