| Early-age cracking can be a significant problem in concrete pavements, floors, and bridge decks. Cracking occurs when the volumetric changes associated with drying, hydration, and temperature reduction are prevented. Good knowledge about the characteristics of early age concrete is necessary to achieve reliable crack control. Volumetric changes due to shrinkage depend on the type of concrete and its components. It has been found that light weight aggregates can work as internal reservoir to supply the concrete matrix with water that is needed during the early age; this process is called internal curing. Also fibers can give more ductility to the concrete and produce less shrinkage.;There is a need to better understand the effects of early age uniaxial restraint on long term concrete mechanical performance. In this study, two types of concrete were studied (high performance fiber reinforced concrete and ordinary concrete) under actively restrained loading conditions to assess the effect on the long term fracture toughness and energy. Single edge notched specimens having dimensions of 250 mm x 150 mm x 75 mm and a notch to depth ratio of 0.33 were caste and used in both direct tension and three point bending. The direct tension tests were carried out on a direct tension loading frame constructed in house that was supplied with two mechanical jacks and load cell. |