Engineering of lead chalcogenide nanostructures for carrier multiplication: Core/shell, 1D, and 2D

Near infrared emitting semiconductors have been used widely in industry especially in solar-cell fabrications. The efficiency of single junction solar-cell can reach the Shockley-Queisser limit by using optimum band gap material such as silicon and cadmium telluride. The theoretical efficiency can be further enhanced through carrier multiplication, in which a high energy photon is absorbed and more than one electron-hole pair can be generated, reaching more than 100% quantum efficiency in the high energy region of sunlight. The realization of more than unity external quantum efficiency in lead selenide quantum dots solar cell has motivated vast investigation on lowering the carrier multiplication threshold and further improving the efficiency.;This dissertation focuses on synthesis of lead chalcogenide nanostructures for their optical spectroscopy studies. PbSe/CdSe core/shell quantum dots were synthesized by cation exchange to obtain thick shells (up to 14 monolayers) for studies of visible and near infrared dual band emissions and carrier multiplication efficiency. By examining the reaction mechanism, a thermodynamic and a kinetic model are introduced to explain the vacancy driven cation exchange. As indicated by the effective mass model, PbSe/CdSe core/shell quantum dots has quasi-type-II band alignment, possessing electron delocalized through the entire quantum dot and hole localized in the core, which breaks down the symmetry of energy levels in the conduction and valence band, leading to hot-hole-assisted efficient multi-exciton generation and a lower carrier multiplication threshold to the theoretical value.;For further investigation of carrier multiplication study, PbTe, possessing the highest efficiency among lead chalcogenides due to slow intraband cooling, is synthesized in one-dimensional and two-dimensional nanostructures. By using dodecanethiol as the surfactant, PbTe NRs can be prepared with high uniformity in width and resulted in fine quantum confinement features. The reaction can be explained by a soft-template assisted process, in which the lamellar lead-thiolate precursor transforms into rod-shape micelle in the existence of telluride anions by electrostatic attraction. Fine tuning the reaction condition by changing the solvent to oleylamine, lead telluride nanowires with length up to 200 nm can be prepared, which bundled together because of the strong dipole-dipole attraction between nanowires. Decreasing the amount of surfactant dodecanethiol in the synthesis produces lead telluride nanorings, which formed by attaching four small particles together, leaving the center void. To prepare two-dimensional nanoplatelets, mixture ligands containing two amines with different carbon chain length were used, which initiate oriented attachment of the nanoparticles to form square-shape nanoplatelets. By further adopting stronger binding ligands such as phosphonic acid, PbTe nanoplatelets with micrometer lateral dimension were prepared with extremely sharp near infrared photoluminescence (less than 40 meV), which has never be achieved in quantum dots and other nanostructures.