Self-assembly of ordered nanostructures

Several different kinds of nanostructure materials were studied in this thesis: self-assembled monodispersive nanocrystals, photonic crystals, ordered mesoporous silica and hierarchically ordered nanostructured materials.; Tetrahedral nanocrystals of CoO, with edge-lengths of 4.4 ± 0.2 nm, were synthesized at high purity and monodispersity. The size, shape and phase selections of the nanocrystals were performed using a novel magnetic field separation technique. These nanocrystals behave like molecules, forming a face-centered cubic self-assembly of nanocrystal superlattices. In-situ behavior of self-assembled CoO nanocrystal arrays was also analyzed using transmission electron microscopy and associated techniques. The surface passivation layer started to evaporate/decompose at temperatures as low as ∼200°C, but the exposed cores of nanocrystals preserved the geometrical configuration of the assembly due to the strong adhesion of the carbon substrate. As the temperature is further increased from 300 to 600°C, the intrinsic crystal structure of the CoO nanoparticles experiences a replacement reaction, resulting in the formation of cobalt carbides. Two-dimensional self-assembling of cobalt nanocrystals with an average particle size of 9.2 nm and polydispersity of 9% is processed.; Phtonic crystals were processed by a template-assisted method. Ordered self-assembly of pores of titania nanocrystals formed a face-centered cubic packing structure. The walls of the pores were made of anatase nanocrystals of ∼8 nm in diameter. Cobalt can be doped into the walls of the pores by solution infiltration of cobalt carbonyl. Cobalt titanium oxide may be formed on the internal surface of the ordered pore structure. This type of structure is likely to be an excellent supporting material for catalysis. The experimental results suggest that transition metal elements can be incorporated into porous titania without blocking the interconnected pores.; Hierarchically ordered nanostructured materials with high porosity at dual length-scale were prepared by a single annealing procedure. The plasma energy of this porous materials shifts about 1.2 eV to lower energy, compared to the fully densed silica spheres. This type of material is expected to have not only large surface area for catalysis, but also low dielectric constant for low-loss dielectric applications.