| A brief introduction to carbon chemistry is given with an emphasis on the use high-temperature reactions that use carbon vapor, generated from graphite, to synthesize nano-structured materials.; Laser and electric are ablation of graphite was utilized to create a variety of high carbon content materials ranging from discrete acetylenic molecules to extremely large multi-wall nanotubes. A new synthesis for large carbon nanotubes, containing 1--5 atom percent nitrogen bound into the graphite lattice, was realized by the reaction of carbon vapor, nickel/yttrium catalyst and cyanogen gas. These carbon "megatubes" were then employed as a substrate to tether a wide variety of molecules both inorganic and organic. The megatubes, in their native and derivatized states, were then assembled into simple circuits to explore their electronic transport properties.; Direct fluorination was used to post-treat the surface of the multi-wall carbon nanotubes in order to alter the inherent physical and chemical properties of the tubes, as well as to serve as another route to functionalize their surfaces. Fluorine sites on the walls of the tube were allowed to react with Grignard reagents to produce nantoubes with the chosen alkyl chemically bonded to the surface. Products were characterized with techniques similar to unfluorinated tubules.; Using similar carbon vaporization techniques, sp-hybridized carbon chain compounds were synthesized. Using a one-step method dicyanopolyynes were synthesized and characterized with nuclear magnetic resonance and mass spectroscopy, containing up to 8 acetylenic repeat units. A two-step method was also utilized to create polyynes terminated with trifluoromethyl or nitrile radicals generated in a capacitively coupled radio frequency glow plasma discharge. A partial characterization of these products was accomplished with nuclear magnetic resonance, mass, and infrared spectroscopy techniques. |