| Nanocomposites have shown promise as the active layer for photovoltaic energy conversion. Devices consisting of CdSe nanocrystals and semiconducting polymer, and devices consisting of C60 and semiconducting polymer have been recently investigated. This work will present the rational design, synthesis, fabrication and characterization of a nanocomposite photovoltaic device-containing Poly 3-hexylthiophene (P3HT), Cadmium Selenium (CdSe) nanocrystals, and C60. The use of these three components allows for a dedicated light harvester, CdSe nanocrystals, a dedicated hole transporter, P3HT, and a dedicated electron transporter, C60. Two primary premises were investigated in this work; first what effect the size of the nanocrystal would have on the efficiency of the devices and second would the addition of C 60 to a CdSe nanocrystal/semiconducting polymer device increase the efficiency of the devices. Three sizes of CdSe nanocrystals (30A, 45A, and 72A) were used in the photoactive layer. Five different composites were used for the photoactive layer ranging from 20% CdSe or C60 to 80% CdSe or C60 of each size of CdSe nanocrystal, while the percentage of P3HT was held constant at 20%. All of the composites were tested at 514 nm at 5 W/m2 and at the industry standard of AM 1.5 at 1000 W/m2 (1 sun). After all the results were analyzed, it was seen that with the addition of C60 only a small percentage of CdSe nanocrystals would be required to make an efficient device, thus making this device cost effective and with more research a viable new source of photovoltaic energy. |