An experimental investigation into the behavior of concrete elements rerofitted with NSM composite strips at elevated temperatures

Near-surface-mounted (NSM) fiber reinforced polymer (FRP) is another strengthening alternative of externally bonded fiber reinforced polymers. NSM FRP is a promising alternative technology that has emerged for enhancing the strength capacity of concrete structures. Most laboratory researches have focused mainly on the overall member performance and/or the bonding performance of the NSM bars or strips. Limited research has focused on the effect of temperature exposure on NSM FRP performance. The results of an experimental program performed on forty-eight (48) concrete block specimen with NSM carbon-fiber reinforced polymer (CFRP) strengthening systems at elevated temperatures that reaches to 200°C [392°F] to investigate flexural performance. The effect of using two different adhesive systems (epoxy anchoring system) with manufacturer recommendation at ordinary and high temperature exposures is also studied. The adhesive was injected in a NSM groove size (25 mm [1 in] deep x 13 mm [0.5 in] wide) the width and depth of the groove were greater than 3 and 1.5 times the CFRP thickness and width, respectively. Test results show that the interfacial strength of the specimens bonded with the ordinary epoxy is maintained until 75°C [167°F] is reached, while the strength noticeably decreases with an increasing temperature above this limit. The specimens with the high-temperature epoxy preserve interfacial capacity up to 200°C [392°F] despite a trend of strength-decrease being observed. The failure of the test specimens is brittle irrespective of adhesive type. Interfacial damage is localized along the bond-line with the presence of hairline cracks that further develop when interfacial failure is imminent.;This thesis also presents an experimental result concerning the bond performance of concrete-adhesive at elevated temperatures that reaches to 200°C [392°F] applied for three hours. Then, the concrete prisms were tested under three point flexural loading. The experimental program is comprised of seventy-two (72) specimens bonded with low viscosity, high viscosity adhesives and high-temperature adhesive and their comparative performance is of interest in the present investigation. Emphasis is placed on the residual capacity of the conditioned bond-concrete interface and corresponding failure mode. For high temperature exposure, it is shown that the high temperature laminated adhesive outperforms the high and low viscosity adhesives by remaining fairly consistent and allowing the strengthening system to remain effective for up to three hours of 200°C [392°F].