Investigation of wide band gap semiconductors: Electrical, optical, and structural properties

Wide band gap semiconductors are important for many device applications, particularly for lasers and light emitting diodes. In this thesis, we studied (1) the enhancement, by thermal annealing, of p-type doping in Mg-doped GaN grown by metal-organic chemical vapor deposition (MOCVD), (2) the formation of type-II ZnTe quantum dots (QDs) in Zn-Se-Te multilayers with submonolayer insertion of ZnTe, as well as the mechanism of the increase of acceptor incorporation in such samples, (3) optical properties of colloidal-synthesized ZnO nanocrystals.; For GaN:Mg grown by MOCVD, it is found that atomic hydrogen, generated during growth, acts as a compensating donor and thus increases the solubility of the acceptor dopant; subsequent to the growth, H can be easily removed and leaves Mg in excess of its equilibrium solubility.; For Zn-Se-Te multilayers with submonolayer insertions of ZnTe, it is found that type-II ZnTe QDs are formed even with only one deposition cycle of submonolayer ZnTe. However, the density of QDs in this case is lower than for samples with three consecutive deposition cycles of ZnTe. Moreover, for Zn-Te-Se multilayers where N is deposited together with Te, it is found that N (acceptor dopant) is embedded in ZnTe-rich nanoislands, a material readily doped p-type. We note that only minimal amounts of Te are incorporated in the overall epitaxial film; thus the overall energy gap remains close to that of pure ZnSe.; Finally, we studied the optical properties of collidal-synthesized nanocrystals of ZnO, a material of great interest because of its large energy gap (∼3.36 eV at room temperature (RT)) together with a high exciton binding energy (∼60 meV at RT). The photoluminescence (PL) of all our samples consists of a dominant near-band-edge UV emission and a weak broad green emission. The origin of the observed green emission is investigated, and attributed to oxygen vacancies near the surface. A simple model for the recombination process, involving free holes and oxygen vacancies, is proposed. Also the size of the ZnO spherical nanoparticles is estimated from the peak position of the green PL. The results are in good agreement with those from TEM measurements.