Study On Hardenability And Mechanical Properties Of 42CrMo Steel For Large-Scale Wind Power Bolts

42CrMo steel has a good combination of strength and toughness after quenching and tempering treatment,which make it an ideal candidate material for high strength bolt.Nevertheless,with the increase of bolt diameter in wind power field,the hardenability of 42 CrMo steel is inadequate to manufacture the high strength bolt with diameter over 36 mm.Recent study indicates that Al addition is an economical and effective way to affect the phase transformation product during quenching process.In order to improve the hardenability of 42 CrMo bolt steel,the effect of Al on the hardenability of 42 CrMo was investigated by Jominy test and cross section hardness distribution test.OM and SEM were used to analyze the morphology of the grain size;chemical phase analysis test was used to detect the precipitation in Al addition steels;the isothermal transformation diagram(TTT curve)was measured to study the phase transformation of the steels;the three dimensional atom probe(3DAP)was used to analyze the Al distribution in matrix;the tensile and impact toughness properties of Al steels were also examined.It was found that the hardenability of 42 CrMo bolt steel could be improved significantly by Al-Ti and Al-B addition,The hardenability of 5 # steel addition with Al-B was the best.After direct quenching,the martensite structure in the core of the cross section is greater than 90%.The improvement of hardenability for Al-Ti steel can be attributed to the increasing dissolved Al content in the matrix because of the Ti addition,which suppresses the formation of bainite during the quenching process.The hardenability of Al-B steel is better than that of Al-Ti steel,which can be ascribed to the dissolved Al and B inhibiting the phase transformation of ferrite and pearlite.Moreover,Al can play an important role in increasing dissolved B content by means of AlN formation,in which the dissolved Al dispersive distribution in matrix is favorable to improve the hardenability of 42 CrMo steel.Meanwhile,the Tensile Strength and Charpy V-notch impact energy at –40? of Al addition steels are adequate to manufacture grade 12.9 high strength bolt.