Corrosion And Fouling Behaviors Of Fluorinated Polysiloxane Coating On Phosphatized Q235 Carbon Steel

Corrosion and fouling problems,which exist in many industrial processes,severely impede industrial production and solving these problems is necessary and meaningful.In this study,various fluorinated polysiloxane coatings with hydrophobic characteristic were fabricated and coated on phosphatized Q235 carbon steel to improve the corrosion resistance and antifouling performances.The phosphatization of carbon steel was to immerse the sample into phosphating solution for a certain time at 30 oC.The fluorinated polysiloxane coating was fabricated via curing fluorinated polysiloxane sol coated on sample.After corrosion and fouling tests,the better performances of corrosion resistance reflected by higher electrochemical impedance and antifouling presented by less fouling adhesion for coated sample were displayed.Moreover,microscopic morphologies,chemical components,thermal stabilities,surface energies,roughness and adhesiveness of fluorinated polysiloxane coatings were also investigated.The fluorinated polysiloxane coating shows good microscopic uniformity,thermal stability with only 6.1 % weight loss at 375 °C and adhesion on substrate.