Environmentally induced crack propagation in Inconel alloys 600 and 690 under hydrogen supersaturated steam

Posted on:2005-05-20Degree:Ph.DType:Dissertation
University:The University of Wisconsin - MilwaukeeCandidate:Ali, Mehboob MuzzammilFull Text:PDF
GTID:1451390008983698Subject:Engineering
Abstract/Summary:
Intergranular stress corrosion cracking (IGSCC) of Inconel alloys 600 and 690 was investigated by exposing them to 300--400°C in deaerated hydrogen supersaturated steam. Crack growth rates were measured in-situ for the above alloys using modified wedge-opening-loaded (M-WOL) linear elastic fracture specimens under constant displacement conditions. The applied stress intensity factors (K) used varied from 29--90 MPam1/2.; An activation energy of 120 kJ/mol was found for crack growth rates as a function of temperature. This activation energy is close to the one corresponding to grain boundary self diffusion of nickel. In addition, it was found that the apparent crack growth rates (da/dt) exhibited a linear dependence with KI, given by (da/dt) = A.KIn, where n = 1 in our case. Microstructurally, crack propagation in both the alloys was predominantly along the grain boundaries. It is suggested that high fugacity hydrogen was generated at the tip of the crack, as a result of the reaction of H2O with Cr2O3 on the fracture surface leading to IGSCC. It was found that the rates of crack propagation in both alloys 600 and 690 are very similar. Moreover, under the applied KIs, both alloys 600 and 690 show a similar tendency to crack intergranularly in a direction perpendicular to the applied stress. Crack branching was also exhibited by both the alloys 600 as well as 690. The difference in the crack growth rates of alloys 600 and 690 was found to be only about 2%, which indicates that the crack growth rates in these alloys is independent of the alloy chromium content and that, possibly very similar crack growth mechanisms are active in both the alloys 600 and 690 under similar conditions of KI and temperature. HREM images at the crack tip of alloy 690 exhibit two distinct regions---a crystalline region, and an adjacent amorphous region, which is likely to be either a hydroxide or an amorphous oxide layer. This layer is expected to result from passivation reactions as the crack surface is exposed to the corrosive environment.
Keywords/Search Tags:Crack, Alloys, Hydrogen
Related items