Processing, microstructure evolution and properties of nanoscale aluminum alloys

In this project, phase transformations and precipitation behavior in age-hardenable nanoscale materials systems, using Al-Cu alloys as model materials, were first studied. The Al-Cu nanoparticles were synthesized by a Plasma Ablation process and found to contain a 2∼5 nm thick adherent aluminum oxide scale, which prevented further oxidation. On aging of the particles, a precipitation sequence consisting of, nearly pure Cu precipitates to the metastable theta' to equilibrium theta was observed, with all three forming along the oxide-particle interface. The structure of theta' and its interface with the Al matrix has been characterized in detail. Ultrafine Al-Cu nanoparticles (5∼25 nm) were also synthesized by inert gas condensation (IGC) and their aging behavior was studied. These particles were found to be quite stable against precipitation.; Secondly, pure Al nanoparticles were prepared by the Exploding Wire process and their sintering and consolidation behavior were studied. It was found that nanopowders of Al could be processed to bulk structures with high hardness and density. Sintering temperature was found to have a dominant effect on density, hardness and microstructure. Sintering at temperatures >600°C led to breakup of the oxide scale, leading to an interesting nanocomposite composed of 100∼200 nm Al oxide dispersed in a bimodal nanometer-micrometer size Al matrix grains. Although there was some grain growth, the randomly dispersed oxide fragments were quite effective in pinning the Al grain boundaries, preventing excessive grain growth and retaining high hardness. Cold rolling and hot rolling were effective methods for attaining full densification and high hardness.; Thirdly, the microstructure evolution and mechanical behavior of Al-Al 2O3 nanocomposites were studied. The composites can retain high strength at elevated temperature and thermal soaking has practically no detrimental effect on strength. Although the ductility of the composite remains quite low, there was substantial evidence for high localized plasticity. The strengthening mechanisms of the composite include: Orowan strengthening, grain size strengthening and Forest strengthening.; Finally, the microstructure evolution and mechanical behavior of 2024Al-Al 2O3 nanocomposites were studied. This 2024Al-Al2O 3 composite exhibits similar thermal stability and high strength at elevated temperature as Al-Al2O3. On aging, the matrix of 2024Al-Al2O3 composites revealed a precipitation sequence of: alphaAl → GP/GPB → theta'/S' → theta/S. The strengthening mechanisms of the 2024Al-Al2O3 composites include precipitation strengthening, Orowan strengthening, grain size strengthening and Forest strengthening.