| In this dissertation, novel biomaterials are designed for bone biomaterials and bone tissue engineering applications. Novel biomaterials of hydroxyapatite with synthetic and natural polymers have been fabricated using a combination of processing routes. Initially, we investigated hydroxyapatite-polycaprolactone-polyacrylic acid composites and observed that minimal interfacial interactions between polymer and mineral led to inadequate improvement in the mechanical properties. Bioactivity experiments on these composites showed that the presence of functional groups, such as carboxylate groups, influence bioactivity of the composites. We have developed and investigated composites of hydroxyapatite with chitosan and polygalacturonic acid (PgA). Chitosan and PgA are biocompatible, biodegradable, and also electrostatically complementary to each other. This strategy led to significant improvement in mechanical properties of new composites. The nanostructure analysis using atomic force microscopy revealed a multilevel organization in these composites. Enhancement in mechanical response was attributed to stronger interfaces due to strong electrostatic interaction between oppositely charged chitosan and PgA. Further analysis using the Rietveld method showed that biopolymers have marked impact on hydroxyapatite crystal growth and also on its crystal structure. Significant changes were observed in the lattice parameters of hydroxyapatite synthesized by following biomineralization method (organics mediated mineralization). For scaffold preparation, chitosan and PgA were mixed first, and then, nano-hydroxyapatite was added. Oppositely charged polyelectrolytes, such as chitosan and PgA, spontaneously form complex upon mixing. The poly-electrolyte complex exists as nano-sized particles. Chitosan/PgA scaffolds with and without hydroxyapatite were prepared by the freeze drying method. By controlling the rate of cooling and concentration, we have produced both fibrous and sheet-containing scaffolds. Hydroxyapatite-containing chitosan/PgA scaffolds maintained their structural integrity under wet conditions. These scaffolds showed extremely porous (97.4%) and interconnected architecture. These scaffolds also promoted cell adhesion, proliferation and differentiation, Osteoblast cells formed nodular structure on thin films and scaffold. Mineralization of these nodules was confirmed by alizarin red S staining. Even after 20 days of seeding, all the cells were found alive. Our results indicated that chitosan-PgA-hydroxyapatite composite scaffolds have high potential for bone tissue engineering. This dissertation represents a comprehensive study on design of novel bone biomaterials through tailoring of interfaces in nanocomposites of polymers, biopolymer and hydroxyapatite. |