Magnetostriction and corrosion studies in single crystals of iron-gallium alloys

Iron-gallium alloys have an excellent combination of large low-field magnetostriction, good mechanical properties, low hysteresis, and relatively low cost. This dissertation focuses on the magneto striction and corrosion behaviors of single crystals of Fe-Ga alloys.; In the first part, the variation of magnetostrictive coefficient: (3/2) lambda100, with composition and heat treatment conditions of Fe-Ga alloys, is examined. Single crystals with compositions Fe-15 at.% Ga, Fe-20 at.% Ga, and Fe-27.5 at.% Ga were obtained by (a) vertical Bridgman technique (DG) and (b) vertical Bridgman technique followed by long-term annealing (LTA) and quenching. Rapid quenching from a phase region improves the (3/2) lambda 100 value in these alloys. X-ray diffraction characterization showed for the first time the direct evidence of short-range ordering in these alloys.; The second part reports the first study of alpha" ordering heat treatment on the elastic properties and magnetostriction of Fe-27.5 at.% Ga alloy single crystals. The elastic constants were measured using resonant ultrasound spectroscopy (RUS), and the elastic properties and magneto-elastic coupling constant were calculated. The (3/2) lambda100 and B1 values obtained for a phase were higher than alpha" phase.; The third part examines the first study of corrosion behavior of as-cast FeGa and Fe-Ga-Al alloys in acidic, basic, and simulated seawater environments. Corrosion measurements were performed by Tafel scan and polarization resistance method and in general exhibited good corrosion resistance.; The fourth part examines the first study of corrosion behavior of Fe-15 at.% Ga, Fe-20 at.% Ga, and Fe-27.5 at.% Ga DG and LTA alloy single crystals and the dependence of corrosion rates on the crystal orientations. The corrosion resistance was better in basic environments followed by simulated seawater and acidic environments.; The fifth part examines the effect of magnetostriction on the corrosion behavior of [100]-oriented single crystal of Fe-20 at.% Ga alloy in acidic and simulated seawater solution, first study ever of this kind. Magnetostrictive strain introduced on the application of saturation magnetic field increased the corrosion rate of [100]-oriented Fe-20 at.% Ga alloy single crystal by 40% in 0.1M HCl and decreased the corrosion rate by 15% in 3.5 wt.% NaCl solution.