Phenomenological studies of hot tearing during solidification of magnesium alloys

There is a renewed interest in magnesium alloys in the automotive industry. Magnesium alloys are ∼35% lighter than aluminum and ∼80% lighter than steel. As a result, incorporation of magnesium alloy castings in new vehicles plays a critical role in reducing the overall vehicle weight and increasing the vehicle's fuel efficiency. Magnesium alloys processed via permanent mold casting (PMC) show a high susceptibility to hot tearing. While several techniques are used to relieve hot tearing (e.g., preheating of molds, grain refinement or elimination of sharp features in part design), the underlying mechanisms responsible for hot tearing remain unclear. In the case of magnesium alloys, limited work has been carried out to advance the fundamental understanding of hot tearing.;The results indicate that the mold temperature had a profound influence on the nucleation of hot tears. When the cooling rate of the AZ91D casting reached ∼15.1°C/s (210°C mold temperature), the fraction of solids development was sufficiently fast to prevent adequate long-range interdendritic feeding of the casting. As a result, shrinkage porosity formed. Shrinkage porosity forming at a location of a stress concentration provided a nucleation site for a hot tear. The stress required to open a shrinkage pore into a hot tear at the stress concentration was ∼ 8--12 MPa. Increasing the mold temperature to 250°C decreased the cooling rate, improved interdendritic feeding of the casting, decreased solidification shrinkage and decreased the magnitude of tensile stresses developing in the casting. In the case of the AE42 alloy, interdendritic feeding of liquid was hindered by the Alx REy intermetallic compounds blocking the interdendritic paths. Further, the presence of acicular Al11RE3 phase pinning the grain boundaries decreased the ductility of the AE42 alloy. As a result, a very slow casting cooling rate (∼ 7.7°C/s) was required to prevent the nucleation of hot tears. For higher cooling rates, hot tears nucleated at locations of stress concentrations and propagated along interdendritic regions and grain boundaries.;This research investigated the influence of alloy microstructure, casting solidification and casting stresses on the onset of hot tearing in AZ91D and AE42 magnesium alloys. A novel approach to determine casting stresses using neutron diffraction was implemented. A custom designed permanent mold was used to manipulate the cooling rate of a casting and ensuing susceptibility to hot tearing.