Fine tuning the heavy fermion ground state: A new handle on cerium cobalt indium

A Two Fluid Description of the Kondo Lattice CeCoIn5 has been extended to include additional entropy terms that were not considered in the original work by S. Nakatsuji et al. [1]. The use of a Matlab computer code was successful at iteratively solving for f, the fraction of itinerant interacting heavy quasiparticles, and showed that it converges to a temperature dependent function invariant under successive iterations. The linear specific heat coefficient, gamma, was extracted from transport consideration in conjunction with f(T) and the Kadowacki-Woods ratio to be 204mJ/mole-K2, in good agreement from heat capacity measurements of 290mJ/mole-K2 for CeCoIn 5 [32].; Antiferromagnetism has been induced in CeCoIn5 as well as its two isostructural, isovalent sister compounds CeRhIn5 and CeIrIn 5. Cadmium-doping the heavy-fermion superconductor CeCoIn5 at the percent level acts as an electronic tuning agent, sensitively shifting the balance between superconductivity and antiferromagnetism and opening new ambient-pressure phase space in the study of heavy-fermion ground states. At nominal concentrations of x>0.070, CeCo(In1-xCd x)5 displays a two phase region of antiferromagnetism coexisting with superconductivity up to x<0.15, above which no trace of superconductivity persists in specific heat. Similar results was seen in CeIr(In1-xCd x)5 where a quantum critical point (QCP) was observed, separating superconductivity from antiferromagnetism at a nominal critical concentration of x≈0.0475, while CeRh(In1-xCdx)5 goes through an incommensurate to commensurate antiferromagnetic transition nominally at x≈0.10. Amazingly, pressure completely recovers Tc in CeCo(In1-x Cdx)5 measured at nominal concentrations of x=0.10, and 0.15. Phase diagrams were constructed from specific heat and confirmed with resistivity and magnetization.; An introduction to strongly correlated physics, relevant to the 115 family, will be worked out followed by a description of general techniques of synthesis and physical properties measurements central to this dissertation and in the study of material science in general.