Nonlinear optical studies of dye-doped nematic liquid crystals

In this dissertation, nonlinear optical studies were carried out on dye-doped nematic liquid crystal cells. The main objectives of the studies were to distinguish and characterize the several processes that can lead to the formation of dynamic gratings of different types in the samples, and to study the photorefractive and the orientational responses of these samples.; Asymmetric two-beam coupling experiments revealed that the induced grating was a photorefractive phase grating created by the nematic director reorientation within the plane of incidence. The dynamics of the beam coupling showed that two different mechanisms with different temporal responses were involved. The grating translation technique identified both gratings as pure photorefractive index gratings with phase shifts of ∼π/2 between the grating and the interference pattern. In addition, the dynamical behavior of the grating formation, obtained from forced light scattering experiments, also exhibited a two-time constant response. The dynamical behaviors of the build-up and decay of the photocurrent were investigated. The two dynamics exhibited both a two-time constant behavior, suggesting that the origin of the two-time constant dynamics observed in the two-beam coupling and the forced light scattering experiments resides in the process of photo-charge generation.; All the samples showed a threshold behavior with respect to the magnitude of the applied electric field. This threshold behavior was observed both in forced light scattering experiments and polarization holographic experiments. We believe that the origin of this threshold lies in the process of photogeneration, which was found to exhibit the same threshold behavior at the same value of the applied voltage. An asymmetry of the photorefractive gain with respect to the direction of the applied electric field was observed in samples with high dye concentration. This was attributed to the beam fanning effect, which has also been observed in other high-gain photorefractive materials.; The conductivity and the photoconductivity of the samples were measured. The photocurrent was found to increase linearly with the illumination power, which indicates that the charge carrier recombination rate is proportional to the carrier density. The measured electrical conductivity was found to be proportional to the square root of the dye concentration, confirming the validity of the proposed charge-injection model. (Abstract shortened by UMI.)...