| Commercial GaN based electronic and optoelectronic devices possess a high density (107-109 cm-2) of threading dislocations (TDs) because of the large mismatch in the lattice constant and the thermal expansion coefficient between the epitaxial layer structure and the substrate. In spite of these dislocations, high brightness light emitting diodes (LEDs) utilizing InGaN or AlGaN multiple quantum wells (MQWs) and with an external quantum efficiency of more than 40%, have already been achieved.;This high external quantum efficiency in the presence of a high density of dislocations has been explained by carrier localization induced by indium fluctuations in the quantum well. TDs have been found to increase the reverse leakage current in InGaN based LEDs and to shorten the operating lifetime of InGaN MQW/GaN/AlGaN laser diodes. Thus it is important that the TD density is further reduced. It remains unclear how the TDs interact with the device to cause the effects mentioned above, hence the careful and precise characterization of threading defects and their effects on the electrical and optical performances of InGaN/GaN MQW LEDs is needed. This investigation will be useful not only from the point of view of device optimization but also to develop a clear understanding of the physical processes associated with TDs and especially with their effect on leakage current.;We have employed photoelectrochemical (PEC) etching to accurately measure the dislocation density initially in home-grown GaN-based epitaxial structures and recently in InGaN/GaN MQW LEDs fabricated from commercial grade epitaxial structures that were supplied by our industrial collaborators. Measuring the electrical and electroluminescence (EL) characteristics of these devices has revealed correlations between some aspects of the LED behavior and the TD density, and promises to allow a deeper understanding of the role of threading dislocations to be elucidated.;We observed that the LED reverse leakage current increased exponentially, and electroluminescence intensity decreased by 22%, as the TD density in the LEDs increased from 1.7 x 107 cm-2 to 2 x 108 cm-2. Forward voltage remained almost constant with the increase of TD density. A model of carrier conduction via hopping through defect related states, was found to provide an excellent fit to the experimental I-V data and provides a useful basis for understanding carrier conduction in the presence of TDs. |